Hot sale! fused AZS Refractory Brick Used for Glass kiln

May 28, 2020

fused AZS Refractory Brick  Used for Glass kiln

 Fused Cast AZS bricks
Fused Cast AZS Refractory bricks products of AZS series of oxidation are made of qualified raw materials by using specially designed electric arch furnace and undergoing the casting process through long-arc melting furnace and oxidation. This kind of casting process hardly suffers any carbon pollution from the electrode

Due to the application of such casting technology and high-purity raw materials, AZS brick of oxidated electrocast zirconia-alumina products are possessed of special and high quality of erosion resistance of glass liquids. In addition, it has the minimal pollution to the glass.

AZS-33 
AZS-33 bricks are excellent in preventing the pollution of glass liquids. The possibility of causing glass stones, bubbles and basic glass phase precipitation is quite slim. It can be applied to the upper structure of melting pool, the tank wall corner tiles,paving bricks and other approaches as well.

AZS-36 
AZS-36 bricks are the standard Fused Cast AZS Refractory bricks brick which boasts of the quality of particularly high corrosion resistance of glass liquids and low pollution. More than that, it has a balanced performance in the above two aspects. It can be applied to the direct access of glass furnace and glass liquids, such as melting tank wall corner tiles, paving bricks and charging door.

AZS-41 
AZS-41 bricks are the best oxidated zircon corundum brick which possesses the quality of highest corrosion resistance of glass liquids and excellent low pollution of glass liquids. It can be applied to the locations of glass furnace which requires particularly high corrosion endurance, such as full-fused furnace, liquid pumps, furnace ridge, bubbling brick and bricks of charging door corners.

 

 

 

AZS brick 009.jpg

 

 

 



















































 

Specification

 

 

Items AZS #41 AZS #36 AZS #33
Al2O3, min 45.50% 48.50% 49.50%
ZrO2, min 41% 36% 33%
SiO2, max 12% 14% 15.50%
Fe2O3, max 0.10% 0.10% 0.10%
TiO2, max 0.05% 0.05% 0.05%
Na2O, max 1.20% 1.30% 1.40%
Bulk Density, g/cm3, min 3.8 3.7 3.6
Apparent Porosity, max 1.00% 1.00% 1.00%
True Density, g/cm3, min 4 3.95 3.85
Cold Crushing Strength, Mpa, min 350 350 350
Softening Temperature Under Load (0.2 Mpa), °C, min 1700 1700 1700
Bubbling Tendency, max 0.50% 0.50% 0.50%
Exudation Temperature of Glass Phase, °C, min 1400 1400 1400
Corrosion Resistance to Glass Melt (mm/24hrs), max 1 1.2 1.3
Thermal Expansion, 1000°C, max 0.80% 0.80% 0.80%
Baddeleyite Crystalline Phase, min 12% 11% 10%
Corundum-Baddeleyite Eutectic Crystalline Phase, min 70% 70% 70%
Glass Phase, max 18% 18% 18%

 

 

 

Characteristic

 

 

fused AZS Refractory Brick  Used for Glass kiln
1. Raw material is corundum and baddeleyite eutecticum,high compression strength
2.Top high-temperature capablility.
3.Excellent thermal stability.
4.Low thermal conductivity
5.Powerful penetrating-proof capability.
6.Good erosion-resistance.
7.Strong resistant erosion stability to the glass liquid.

AZS brick 006.jpg

 

 

Application: 
AZS are applied for the top and bottom structure of melting chamber.Such as melting tank, the tank wall brick, the paving brick,the forehearths and so on.The high corrosion 

part shall be AZS 41#, such as the feeding part, the throat,the bubble brick, the furnace weir, the burner block, the tongue brick and the discharging part and so on.